| About |
|---|
| Grilamid® L XE 10953 black是一种聚酰胺12（尼龙12）材料,。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:挤出。 Grilamid® L XE 10953 black的主要特性有: 阻燃/额定火焰 增塑 冲击改性 高粘度 抗静电 典型应用领域包括: 汽车行业 电线电缆 软管 |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good flexibility,High impact resistance,High Viscosity,Heat Resistance, Good,Antistatic property,Plasticizing |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | |
| Shrinkage rate | |||
| TD | 1.4 | % | |
| MD | 1.1 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 1.2 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.60 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 无断裂 | ||
| Charpy Unnotch Impact strength | |||
| -30℃ | 无断裂 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | |
| 1.8 MPa, unannealed | 45.0 | ℃ | |
| Continuous use temperature | |||
| — | 90.0 to 110 | ℃ | |
| — | 150 | ℃ | |
| Melting temperature | 173 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-4 | 1/℃ | |
| TD | 1.8E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | |
| Volume resistivity | 1.0E+8 | ohms·cm | |
| Dielectric strength | 14 | kV/mm | |
| Compared to the leakage tracing index | — | V |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level (0.8 mm) | HB |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Type | PA12-P,,EHZ,C24-005 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 63 | ||
| Tensile modulus | 500 | MPa | |
| Tensile stress (50% strain) | 30.0 | MPa | |
| Tensile strain | |||
| fracture | > 50 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |