| About |
|---|
| Grilamid® LCL-3 H anthracite is a Polyamide 12 (Nylon 12) material filled with 30% long carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grilamid® LCL-3 H anthracite are: Flame Rated Antistatic Heat Resistant Typical applications include: Automotive Electrical/Electronic Applications Appliances Engineering/Industrial Parts Household Applications&& |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,Antistatic property,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| TD | 0.10 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 1.1 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.60 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | — | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | — | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 170 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 160 | ℃ | ISO 75-2/C |
| Continuous use temperature | |||
| — | 90.0 to 120 | ℃ | ISO 2578 |
| — | 150 | ℃ | Internal Method |
| Melting temperature | 178 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| TD | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | IEC 60093 |
| Volume resistivity | — | ohms·cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | HB | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | — | MPa | ISO 2039-1 |
| Tensile modulus | — | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | — | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | — | % | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Long Term |
| 3. Short Term |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |