| Grilamid® LV-50H FWA nat是一种聚酰胺12（尼龙12）材料,含有的填充物为50% 玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,加工方式为:注射成型。 Grilamid® LV-50H FWA nat的主要特性有: 阻燃/额定火焰 通过 ROHS 认证 可接触食品 热稳定剂 典型应用领域包括: 水管/管道/饮用水 食品接触应用 工业应用 家庭应用 生活消费品&& |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Food contact compliance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.47 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 | ||
| TD | 0.50 | % | ISO 294-4 |
| MD | 0.10 | % | ISO 294-4 |
| Water absorption rate | ISO 62 | ||
| Saturation, 23 ℃ | 0.80 | % | ISO 62 |
| Equilibrium, 23 ℃, 50% RH | 0.40 | % | ISO 62 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 15 | kJ/m² | ISO 179/1eA |
| 23℃ | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| 23℃ | 90 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 165 | ℃ | ISO 75-2/A |
| 8.0 MPa, unannealed | 125 | ℃ | ISO 75-2/C |
| Continuous use temperature | |||
| — | 90.0 to 120 | ℃ | ISO 2578 |
| — | 150 | ℃ | Internal Method |
| Melting temperature | 178 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 1.5E-5 | 1/℃ | ISO 11359-2 |
| TD | 1.2E-4 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | — | ohms | IEC 60093 |
| Volume resistivity | — | ohms·cm | IEC 60093 |
| Dielectric strength | — | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | — | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | |||
| 0.8 mm | HB | IEC 60695-11-10, -20 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | — | ISO 868 | |
| Ball hardness | — | MPa | ISO 2039-1 |
| Tensile modulus | 12000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 155 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |