| About |
|---|
| Grivory® GVX-5 H nat is a Polyamide 66 + PA 6I/X (Nylon 66+Nylon 6I/X) material filled with 50% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding. Important attributes of Grivory® GVX-5 H nat are: Flame Rated RoHS Compliant Heat Stabilizer Typical applications include: Automotive Electrical/Electronic Applications Appliances Consumer Goods Engineering/Industrial Parts&& |
| Product Description | |
|---|---|
| Supplier | EMS-GRIVORY |
| Generic | PA 66+PA 6I/X |
| Material Status | Commercial: Active |
| Features | Aromatic,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.56 | g/cm³ | ISO 1183 |
| Shrinkage rate | |||
| MD | 0.1 | % | ISO 294-4 |
| TD | 0.3 | % | ISO 294-4 |
| Water absorption rate | |||
| 23℃，24hr | 4.0 | % | ISO 62 |
| Water absorption rate | 1.4 | % | ISO 62 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, annealed | 245 | ℃ | ISO 75-2/Af |
| Hot deformation temperature | 175 | ℃ | ISO 75-1/2 |
| Melting temperature | 260 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 5.0E-5 | 1/℃ | ISO 11359-2 |
| Maximum operating temperature | 100-120 | ℃ | |
| Maximum operating temperature | 220 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+12 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+12 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 33.0 | KV/mm | IEC 60243-1 | |
| Dissipation factor | |||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.80mm | HB | UL-94 | |
| 0.88mm | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 65 | kJ/m² | ISO 179/1eU |
| Charpy Unnotch Impact strength | |||
| 23℃ | 80 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 290 | MPa | ISO 2039-1 |
| tensile strength | |||
| 23℃ | 250 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 2.5 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 18000 | MPa | ISO 527-2 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Long Term |
| 3. Short Term |
| 4. 10°C/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |