| Polypropylene copolymer high flow 17% mineral filled, high impact resistance and good mechanical properties.&& |
| Product Description | |
|---|---|
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High impact resistance,High liquidity,Copolymer,HB |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 22 | g/10min | ISO 1133 |
| Shrinkage rate | Internal Method | ||
| TD | 0.80 to 1.0 | % | Internal Method |
| MD | 0.60 to 0.80 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.050 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 25.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 35 | % | ISO 527-2/50 |
| Bending modulus | 1500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 120 | J/m | ASTM D256 |
| 0℃ | 170 | J/m | ASTM D256 |
| 23℃ | 250 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 75.0 | ℃ | ISO 75-2/A |
| Continuous use temperature | 80.0 | ℃ | IEC 60216 |
| Vicat Softening Temp | |||
| A50 | 135 | ℃ | ISO 306/A50 |
| B50 | 53.0 | ℃ | ISO 306 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Ash Content | |||
| 600℃ | 17 | % | ISO 3451 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 180 to 200 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 3. 20,000 hr |
| 4. 1 hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |