| About |
|---|
| Halar® 700 HC is an Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for extrusion. Important attributes of Halar® 700 HC are: Flame Rated Medium Viscosity&& |
| Product Description | |
|---|---|
| Supplier | Solvay |
| Generic | ECTFE |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.70 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 275℃，2.16kg | 7.0 to 10 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | < 0.10 | % | ASTM D570 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Trouser Tear（23℃，3.20 mm） | 420.0 | kN/m | DIN 53363 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -50.0 | ℃ | ASTM D746A |
| Glass transition temperature | 70.0 | ℃ | DMA |
| Melting temperature | 200 | ℃ | ASTM D3418 |
| Crystallization peak temperature | |||
| DSC | 180 | ℃ | ASTM D3418 |
| Thermal conductivity coefficient | |||
| 23℃ | 0.18 | W/m/K | ASTM C177 |
| Crystallization heat | 22.7 | J/g | ASTM D3418 |
| thermal stability | |||
| 1% mass loss, N2 | 359 | ℃ | TGA |
| Fusion heat | 24.0 | J/g | ASTM D3418 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Dielectric strength | |||
| 23 ℃，3.2 mm | 14 | kV/mm | ASTM D149 |
| Dielectric constant | |||
| 23 ℃，1 MHz | 2.57 | ASTM D150 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 | |
| Extreme oxygen index | > 52 | % | ASTM D2863 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 74 | ASTM D2240 | |
| Tensile modulus | |||
| 23℃ | 1320 | MPa | ASTM D882 |
| tensile strength | ISO 527-3 | ||
| Yield, 23 ℃ | 28.5 | MPa | ISO 527-3 |
| Fracture, 23 ℃ | 41.4 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| Yield, 23 ℃ | 5.0 | % | ISO 527-3 |
| Fracture, 23 ℃ | 310 | % | ISO 527-3 |
| friction coefficient | |||
| With oneself – dynamic | 0.20 | ASTM D1894 | |
| Taber abraser | |||
| 1000 cycles, 500 g, CS-17 wheels | 16.5 | mg | ASTM D4060 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.31 in/min |
| 3. 20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |