| About |
|---|
| M5018L is an Injection Molding Grade HDPE produced by Spherilene Technology. This resin is particularly recommended for general-purpose Injection Molding M5018L combines excellent processability with good mechanical properties.&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.950 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 19 | g/10min | ASTM D1238 |
| Spiral flow length | 60.0 | cm | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, injection molding | 30 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 78.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 5 |
| Melting peak temperature | 132 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, injection molding | 62 | ASTM D2240 | |
| tensile strength | |||
| Yield, injection molding | 22.0 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, injection molding | 350 | % | ASTM D638 |
| Bending modulus | |||
| injection molding | 800 | MPa | ASTM D790-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 180 to 235 | °C | |
| Barrel middle temperature | 180 to 235 | °C | |
| Barrel front temperature | 180 to 235 | °C | |
| Nozzle temperature | 235 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 23°C |
| 3. Melt Temperature: 455°F |
| 4. 2.0 in/min |
| 5. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |