| About |
|---|
| HANWHA LDPE 963 is manufactured by autoclave process and designed for variety of extrusion coating application such as paper and Tarpaulin coating etc. LDPE 963 is well known for its excellent processability and high quality assurance.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | LDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Good heat sealing,Good dissection,Low shrinkage |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | ASTM D638 | ||
| yield | 8.83 | MPa | ASTM D638 |
| fracture | 8.83 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 500 | % | ASTM D638 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Water vapor transmittance | 17 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 85.0 | ℃ | ASTM D1525 |
| Melting temperature | 105 | ℃ | ASTM D3417 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Allowable Coating Speed | 6.7 | m/sec |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 200 to 315 | °C | |
| Barrel 2 zone temperature | 200 to 315 | °C | |
| Barrel 3 zone temperature | 200 to 315 | °C | |
| Barrel 4 zone temperature | 200 to 315 | °C | |
| Barrel 5 zone temperature | 200 to 315 | °C | |
| Connector temperature | 315 | °C | |
| Nozzle temperature | 315 | °C | |
| Shrinkage 2 | 38.0 | mm | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Melt Temperature : 305°C, Line Speed : 100m/min., Output: 80kg/hr |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |