| About |
|---|
| HANWHA LLDPE 3127 is manufactured by Unipol process and designed for lamination film. LLDPE 3127 has well balanced property of optical property and processability.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | Linear low density polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Optical performance,High anti-blocking,Inoxidizability,Low smoothness |
| Availabilitys | Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 30 | µm | Internal Method |
| tensile strength | ASTM D882 | ||
| fracture | 21.6 | MPa | ASTM D638 |
| MD, fracture, 30 µ m | 42.2 | MPa | ASTM D882 |
| TD, fracture, 30 µ m | 37.3 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| fracture | 900 | % | ASTM D638 |
| MD, fracture, 30 µ m | 650 | % | ASTM D882 |
| TD, fracture, 30 µ m | 750 | % | ASTM D882 |
| Drop hammer impact | |||
| 30 µm | 140 | g | ASTM D1709 |
| tear strength | ASTM D1004 | ||
| MD，30 µm | 117.7 | kN/m | ASTM D1004 |
| TD，30 µm | 122.6 | kN/m | ASTM D1004 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -76.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 103 | ℃ | ASTM D1525 |
| Melting temperature | 122 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | |||
| 30 µm | 8.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Blow（up Ratio） | 2.00 to 3.00 | ||
| Optimum Gage Range | 30.0 to 100.0 | µm |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 150 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |