| Hanwha Total’s EVA E182L is designed for conventional T-die extrusion coating process. Proprietary polymerization technology in high pressure tubular process show good optical clarity, adhesion properties and low gel level. Characteristics High productivity Excellent optical properties Low gel level High adhesion strength Well-balanced drawability and neck-in Applications Extrusion coating for food packaging film, kraft paper, aluminium foil and BOPP film&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | EVA |
| Material Status | Commercial: Negative |
| Features | Good Clarity,Optical performance,Low speed solidification point,Good bond,Copolymer |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 15 | g/10min | ASTM D1238 |
| Vinyl acetate content | 18.0 | wt% | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 12.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 600 | % | ASTM D638 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 56.0 | ℃ | ASTM D1525 2 |
| Melting temperature | 83.0 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel temperature | 23 | °C | |
| Nozzle temperature | 230 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |