| About |
|---|
| Description E283F is EVA resin can be used in crosslinked foam applications and wire & cable compounding applications. This grade is designed to be processed in conventional kneading and rolling equipment for mixing and dispersing crosslinking agent/foaming agent and (or) various additives. Characteristics E283F, having 28% VA (vinyl acetate) content offers good processability during compounding with various additives. Foamed products made from this grade provide excellent split tear resistance and good compression set properties. Also, this grade imparts excellent mechanical properties to the finished W&C coat. Applications Athletic shoe unitsole, midsoles, and sandals LSNH (Low Smoke None Halogen) FR (Flame Retardant) W&C compound&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | EVA |
| Material Status | Commercial: Negative |
| Features | Excellent Processability,Crosslinked,Foaming performance,Good Compression Set,Good tear strength,Copolymer |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 3.0 | g/10min | ASTM D1238 |
| Vinyl acetate content | 28.0 | wt% | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -70.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 45.0 | ℃ | ASTM D1525 2 |
| Melting temperature | 70.0 | ℃ | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | ASTM D2240 | ||
| Shaw’s A | 82 | ASTM D2240 | |
| Shaw’s D | 27 | ASTM D2240 | |
| tensile strength | |||
| fracture | 23.5 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 800 | % | ASTM D638 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |