Hanwha Total PP BI740

About
Description BI740 is a highly isotactic block copolymer with high crystalinity. It shows an excellent balance of strength and impact resistance due to the application of high crystalline technology and the most appropriate rubber design. Its excellent gloss and surface hardness also make it useful in the exterior of family appliances. Characteristics Excellent flowability, strength / hardness High flowability/high strength : Allows for larger and thinner injection Molded products High heat resistance – High utilization temperature High crystalinity – Short cooling time after injection molding to allow for high speed production Good surface hardness – Superior scratch resistance Applications Large E&E articles, base resin for PP compound (auto & E&E)&&

About

Description BI740 is a highly isotactic block copolymer with high crystalinity. It shows an excellent balance of strength and impact resistance due to the application of high crystalline technology and the most appropriate rubber design. Its excellent gloss and surface hardness also make it useful in the exterior of family appliances. Characteristics Excellent flowability, strength / hardness High flowability/high strength : Allows for larger and thinner injection Molded products High heat resistance – High utilization temperature High crystalinity – Short cooling time after injection molding to allow for high speed production Good surface hardness – Superior scratch resistance Applications Large E&E articles, base resin for PP compound (auto & E&E)&&

Product Description
Supplier	HANWHA
Generic	HC PP
Material Status	Commercial: Active
Features	Good Rigidity,Good surface appearance,High impact resistance,High liquidity,Good Hardness,Crystal,High Heat Resistance,Block Copolymer,High scratch resistance
Availabilitys	North America,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ASTM D1505
Melt Flow Rate
230℃，2.16kg	25	g/10min	ASTM D1238

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ASTM D256
-20℃	34	J/m	ASTM D256
23℃	59	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	132	℃	ASTM D648

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	97		ASTM D785
tensile strength
yield	33.3	MPa	ASTM D638
Tensile strain
fracture	> 50	%	ASTM D638
Bending modulus	1720	MPa	ASTM D790

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.