Hanwha Total PP FH22

About
FH22 is a highly rigid, high-gloss, and flame retardant polypropylene compound, using a variety of base PPs, such as HIPP (High Isotactic Polypropylene), which are manufactured with SAMSUGN TOTAL`s special processing technology to offer top-of-the-line quality. This product features superior rigidity, heat and scratch resistance and low blooming. In addition to high flowability, FH22 features outstanding processability, flame-retardancy and add to the appearance of the finished product. FH22 is widely used in the exterior parts of electric and electronic products requiring high flame retardant property.&&

About

FH22 is a highly rigid, high-gloss, and flame retardant polypropylene compound, using a variety of base PPs, such as HIPP (High Isotactic Polypropylene), which are manufactured with SAMSUGN TOTAL`s special processing technology to offer top-of-the-line quality. This product features superior rigidity, heat and scratch resistance and low blooming. In addition to high flowability, FH22 features outstanding processability, flame-retardancy and add to the appearance of the finished product. FH22 is widely used in the exterior parts of electric and electronic products requiring high flame retardant property.&&

Product Description
Supplier	HANWHA
Generic	HC PP
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,Good surface appearance,High liquidity,Flame Characteristics,High Heat Resistance,High scratch resistance,Heat Stabilized,V-0
Availabilitys	North America,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.02	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	6.0	g/10min	ASTM D1238
Shrinkage rate
MD：2.0 mm	1.4 to 1.8	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	44	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	120	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
0.79 mm	V-0		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	100		ASTM D785
tensile strength	37.3	MPa	ASTM D638
Tensile strain
fracture	20	%	ASTM D638
Bending modulus	1860	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Barrel rear temperature	170 to 180	°C
Barrel middle temperature	180 to 200	°C
Barrel front temperature	180 to 200	°C
Nozzle temperature	190 to 210	°C
Mold temperature	40 to 70	°C
Injection pressure	39.2 to 78.5	MPa
Back pressure	0.490 to 1.96	MPa

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.