Hanwha Total PP GB35F

About
GB35F is a fire-resistant G/F modified polypropylene compound modified by filling glass fiber to improve mechanical rigidity and heat-resistance. It also possesses excellent flame retardancy. This product can be produced modifying a variety of base PPs, including HIPP (High Isotactic Polypropylene), in HANWHA TOTAL’s special processing technology. G/F modified PP is commonly used in making products such as car switch covers, electric tool housings and the like requiring high rigidity, high heat resistance, flame retardancy for outdoor use, and good weatherability.&&

About

GB35F is a fire-resistant G/F modified polypropylene compound modified by filling glass fiber to improve mechanical rigidity and heat-resistance. It also possesses excellent flame retardancy. This product can be produced modifying a variety of base PPs, including HIPP (High Isotactic Polypropylene), in HANWHA TOTAL’s special processing technology. G/F modified PP is commonly used in making products such as car switch covers, electric tool housings and the like requiring high rigidity, high heat resistance, flame retardancy for outdoor use, and good weatherability.&&

Product Description
Supplier	HANWHA
Generic	HC PP
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Low warping,Excellent Processability,High impact resistance,Flame Characteristics,High Heat Resistance,V-0
Availabilitys	North America,Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.35	g/cm³	ASTM D792
Melt Flow Rate
230℃，2.16kg	5.0	g/10min	ASTM D1238
Shrinkage rate
MD：2.0 mm	0.20 to 0.70	%	ASTM D955

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	98	J/m	ASTM D256

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	160	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level
1.59 mm	V-0		UL 94

MECHANICAL	Nominal value	Unit	Test method
Rockwell hardness
R-level	100		ASTM D785
tensile strength	68.6	MPa	ASTM D638
Tensile strain
fracture	3.0	%	ASTM D638
Bending modulus
23℃	88.3	MPa	ASTM D747
Bending modulus	5000	MPa	ASTM D790

Process Conditions
injection	Nominal value	Unit	Test method
Barrel rear temperature	180 to 220	°C
Barrel middle temperature	180 to 220	°C
Barrel front temperature	180 to 220	°C
Mold temperature	40.0 to 80.0	°C
Injection pressure	58.8 to 108	MPa
Back pressure	0.490 to 0.981	MPa
Screw speed	20 to 70	rpm

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.