| About |
|---|
| Description G/F modified Compound PP is modified by glass fiber filling and to improve mechanical rigidity and heat-resistance. It is produced made by modifying . A variety of base PPs, including HIPP (High Isotactic Polypropylene), with Hanwha Total’s special processing technology. Its excellent quality makes it ideal for use in air conditioner fans and automobile cooling fans; and like products requiring high rigidity and high impact-resistance. Characteristics There is a wide selection of Hanwha G/F PP products available for uses in products that require high- and ultra-high rigidity and high flowability. Adjustments depending upon molding conditions present no difficulty. Several Hanwha Total G/F PPs have improved dimensional stability thanks to blends with mica, and fire-resistance ratings of UL94 V-0. Applications G/F PP helps improve rigidity and impact-resistance simultaneously dimensional stability, while providing heightened heat-resistance. These grades are high-temperature strengths with added. The most common uses are in: Automobile parts, including brackets, switch boxes, cooling fans and oil caps; Electric and electronic parts, such as air conditioner fans, washing machine drums, pulley/legs for washing machines, and more; Household/industrial appliances, parts for electric tools, showers, bidets , etc.&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | HC PP |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Low warping,Excellent Processability,High impact resistance,Good Dimensional Stability,High liquidity,Flame Characteristics,High Heat Resistance,Good Tensile Strength,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.13 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 7.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 0.20 to 0.90 | % | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 130 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 163 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 115 | ASTM D785 | |
| tensile strength | 108 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 5880 | MPa | ASTM D790 |
| bending strength | 147 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 180 to 220 | °C | |
| Barrel middle temperature | 180 to 220 | °C | |
| Barrel front temperature | 180 to 220 | °C | |
| Mold temperature | 50 to 80 | °C | |
| Injection pressure | 49.0 to 88.3 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |