| About |
|---|
| High glossy compound PP SI51C and SH52C are improved heat resistant PP grades. These products have the high heat-resistance required for use in electric heating equipment parts, as well as superior surface gloss and scratch-resistance. These are Korea’s best high heat-resistant, high glossy compound PP products, They are designed for the exterior housing s of household appliances which require an elegant appearance, such as rice cookers, toasters, irons, jars, pots, and bread makers. Applications Rectangular rice cooker housings bodies, bases, and covers Bread-makers, irons, and hot pots Electronic products requiring high heat-resistance, high glossiness, and clear finish&& |
| Product Description | |
|---|---|
| Supplier | HANWHA |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,High impact resistance,Crystal,High Heat Resistance,Durability,High scratch resistance,HB |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 12 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：2.0 mm | 1.3 to 1.5 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 39 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 140 | ℃ | ASTM D648 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 110 | ASTM D785 | |
| tensile strength | |||
| yield | 39.2 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 100 | % | ASTM D638 |
| Bending modulus | 2450 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Barrel rear temperature | 170 to 190 | °C | |
| Barrel middle temperature | 180 to 200 | °C | |
| Barrel front temperature | 180 to 210 | °C | |
| Nozzle temperature | 180 to 210 | °C | |
| Mold temperature | 50 to 70 | °C | |
| Injection pressure | 39.2 to 68.6 | MPa | |
| Back pressure | 0.490 to 1.96 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 3. 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |