| About |
|---|
| GRAFTED HALOGEN FREE, FLAME RETARDANT AND LOW SMOKE EMISSION COMPOUND, CURABLE BY EXPOSURE TO MOISTURE FOR CABLE INSULATION AND SHEATING This product is a LSFOH silane grafted compound for cable insulation and sheating, Cross-linkable by heat and moisture by previous addition of a suitable catalyst masterbatch (SIOPLAS method). It is highly recommended to store separately the grafted compound and the catalyst, as prescorching may take place during the reactive extrusion. The properties of this compound meet the requirements of VDE 0266 type HXI1 & HXM1, EN 50363-0 type G9-G10 & M2, VDE 0207 part 23 type HJ1, BS 50363-5:2005 type EI5, CEI 20-91 type G21-M21, TUV2pfg1169-082007solar insulation and sheath&& |
| Product Description | |
|---|---|
| Generic | 聚烯烃，共挤薄膜用聚烯烃 |
| Material Status | Commercial: Active |
| Features | Low smoke,Crosslinked,Halogen free,Flame Characteristics |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 150℃，21.6kg | 4.5 | g/10min | ISO 1133 |
| Shrinkage rate | |||
| 100℃，1 hrs | < 2.0 | % | IEC 60811 |
| Water absorption rate | |||
| 100℃，24hr | < 5.00 | mg/cm² | IEC 60811 |
| PH value | > 4.3 | EN 50267-2-2 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| thermosetting | IEC 60811 | ||
| Elongation under load: 200 ℃ | 20 | % | IEC 60811 |
| Elongation under load: 250 ℃ | 30 | % | IEC 60811 |
| Maximum permanent elongation after cooling: 200 ℃ | 0.0 | % | IEC 60811 |
| Maximum permanent elongation after cooling: 250 ℃ | 5.0 | % | IEC 60811 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | ASTM D257 | ||
| 20 ℃ | 1.0E+16 | ohms·cm | ASTM D257 |
| 20 ℃ | 5.0E+15 | ohms·cm | ASTM D257 |
| Conductivity | < 10.0 | µS/mm | EN 50267-2-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Extreme oxygen index | 33 | % | ISO 4589-2 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Gas Evolved Acidity | |||
| HCl & HBr | < 0.50 | % | EN 50267-2-1 |
| HF | < 0.10 | % | EN 60684-2 |
| Knife Penetration（100℃） | < 50 | % | IEC 60811 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 15 seconds | 45 | ISO 868 | |
| tensile strength | ISO 527-2 | ||
| fracture | 11.5 | MPa | ISO 527-2 |
| fracture | 13.0 | MPa | ISO 527-2 |
| Tensile strain | ISO 527-2 | ||
| fracture | 280 | % | ISO 527-2 |
| fracture | 250 | % | ISO 527-2 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 120 to 140 | °C | |
| Barrel 2 zone temperature | 120 to 140 | °C | |
| Barrel 3 zone temperature | 130 to 150 | °C | |
| Barrel 4 zone temperature | 130 to 150 | °C | |
| Barrel 5 zone temperature | 130 to 150 | °C | |
| Connector temperature | 130 to 150 | °C | |
| Nozzle temperature | 150 to 180 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |