HB151 - SOLIAO

About
车用喇叭罩，扣手低座，储油罐，电动工具壳体

Product Description
Generic	PA6
Material Status	Commercial: Active
Availabilitys	Asia Pacific

Technical Data
PHYSICAL	Nominal value	Unit	Test method
moisture content	0.7-2.7
Density	1.23±0.02	g/cm³	ISO 1183-1-A
ball indentation hardness	160	MPa	ISO 2039-1
Filler content	15±1	%

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Fracture, dry state	118	MPa	ISO 527-1-2
Fracture, wet state	65	MPa	ISO 527-2
Tensile strain
Fracture, dry state	3	%	ISO 527-1
Wet state	10	%	ISO 527-2
bending strength
Yield, dry state	170	MPa	ISO 178
Yield, wet state	150	MPa	ISO 178
Bending modulus
Dry state	3900	MPa	ISO 178
Wet state	3400	MPa	ISO 178

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa	210	℃	ASTM D648
1.8 MPa	185	℃	ASTM D648

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
Flame retardant level	HB

optical performance	Nominal value	Unit	Test method
Light resistance performance	4

IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength
Dry state	38	kJ/m²	ISO 179-1-1eU
Wet state	75	kJ/m²	ISO 179-1-1eU
Charpy Notched Impact Strength
Dry state	5	kJ/m²	ISO 179-1-1eA
Wet state	10	kJ/m²	ISO 179-1-1eA

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.