| About |
|---|
| Hepla® H3000 is a unreinforced (PTE) product.Characteristics include:Medium Viscosity,Wear Resistant. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PTE |
| Material Status | Commercial: Active |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 60 | g/10 min | ASTM D1238 | |
| 240℃/2.16 kg | |||
| Shrinkage rate MD | 1.8 to 2.0 | % | ASTM D955 |
| Water absorption rate | |||
| 0.5 | % | ASTM D570 | |
| Equilibrium, 23℃, 60% RH | |||
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 105 | ASTM D785 | |
| Tensile Strength (23℃) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Break,23℃) | >270 | % | ASTM D638 |
| Bending modulus 23 ℃ | 1370 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 58.8 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 98.1 | J/m | ASTM D256 | |
| 23℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.00E+15 | ohms·cm | ASTM D257 |
| Dielectric strength | 17 | KV/mm | ASTM D149 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 210 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 105 | ℃ | ASTM D648 |
| Melting Temperature | 220 | ℃ | ASTM D1525 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Injection pressure | 50 to 120 | MPa | |
| Melt Temperature | 220 to 245 | ℃ | |
| Mold temperature | 65 to 108 | ℃ | |
| drying temperature | 110 | ℃ | |
| Drying time | 4 | hr | |
| Dew point temperature | -25 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |