| About |
|---|
| Hepla® H3040GF is a(PTE) product filled with 40% glass fiber.Characteristics include:Medium Flow,Wear Resistant. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PTE |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.57 | g/cm3 | ASTM D792 |
| Mold Shrinkage – 3T,MD/TD | 0.2/1.1 | % | ASTM D955 |
| Water Absorption (23℃, 50%RH） | 0.3 | % | ASTM D570 |
| Melt Flow Rate | |||
| 240℃，2.16kg | 16 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 166 | MPa | ASTM D638 |
| Nominal Strain (Break, 23℃) | 2.3 | % | ASTM D638 |
| Bending modulus 23 ℃ | 8500 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 195 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 16 | KJ/m2 | ISO 179/1eA |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.8 mm | HB | UL 94 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 210 | ℃ | ASTM D648 |
| Melting Temperature | 220 | ℃ | ASTM D1525 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Injection pressure | 50 to 120 | MPa | |
| Melt Temperature | 220 to 245 | ℃ | |
| Mold temperature | 65 to 108 | ℃ | |
| drying temperature | 110 | ℃ | |
| Drying time | 4 | hr | |
| Dew point temperature | -25 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |