| About |
|---|
| Hepla® H5030GF 5TF 2SI is a Acetal (POM) Copolymer product filled with 30% glass fiber and 5% PTFE,2% Silicone.Characteristics include:Lubricated. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.65 | g/cm³ | ASTM D792 |
| water content | 0.15 | % | |
| Shrinkage rate | |||
| MD：3.20 mm | 0.2 to 0.5 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8385 | MPa | ASTM D638 |
| tensile strength | 104.8 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 2 to 2.9 | % | ASTM D638 |
| Bending modulus | 8740 | MPa | ASTM D790 |
| bending strength | 174 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 3.20 mm | 87 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 583 | J/m | ASTM D4812 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5 mm | HB | UL 94 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 163 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Injection pressure | 68.9 to 103 | MPa | |
| Melt Temperature | 182 to 218 | ℃ | |
| Mold temperature | 79 to 107 | ℃ | |
| drying temperature | 121 | ℃ | |
| Drying time | 2 | hr | |
| Dew point temperature | -32 | ℃ | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |