| Hepla ® H7030GF ES is a Polyamide 12 (PA12) material filled with 30% glass fiber and Antistatic Agent.Characteristics include:Antistatic,UV Resistant.It is available in Africa & Middle East,Asia Pacific,Europe,Latin America,or North America for injection molding. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PA12 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Good Dimensional Stability,Low or no water absorption,Solvent resistance,Antistatic property |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm3 | ISO 1183 |
| Water absorption rate | |||
| Balance, 23 ° C, 50% RH | 0.6 | % | ISO 62 |
| Saturation, 23 ° C, 50% RH | 1.1 | % | ISO 62 |
| Shrinkage rate | |||
| MD | 0.1 | % | ISO 294-4 |
| TD | 0.8 | % | ISO 294-4 |
| hardness | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| D-level, 15 seconds | 83 | ISO 868 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 7687 | MPa | ISO 527-2/1 |
| tensile strength | |||
| fracture | 123 | MPa | ISO 527-2/1 |
| Tensile strain | |||
| fracture | 5.1 | % | ISO 527-2/1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 10.2 | kJ/m² | ISO 179/1eA |
| 23℃ | 15.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| -30℃ | 70.5 | kJ/m² | ISO 179/1eU |
| 23℃ | 85.6 | kJ/m² | ISO 179/1eU |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.8 mm | HB | IEC 60695-11-10, -20 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.00E+06 | Ohms•cm | IEC 60093 |
| Surface resistivity | 1.00E+06 | Ohms | IEC 60093 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 8 MPa, 80 * 10 * 4, span 64mm, unannealed | 90 | ℃ | ISO 75/Cf |
| 1.8 MPa, 80 * 10 * 4, span 64mm, unannealed | 160 | ℃ | ISO 75/Af |
| Continuous use temperature | |||
| long-term | 90 to 120 | ℃ | ISO 2578 |
| short-term | 150 | ℃ | NFD Method |
| Melting temperature | |||
| 10℃/min | 178 | ℃ | ISO 11357-3 |
| Linear coefficient of thermal expansion | |||
| MD | 5.00E-05 | 1/℃ | ISO 11359-2 |
| TD | 1.20E-04 | 1/℃ | ISO 11359-2 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |