| Hepla® H7350GF H is a Polyamide 46 (PA46) product filled with 50% glass fiber and Heat Stabilizer.Characteristics include: Heat Stabilizerd. |
| Product Description | |
|---|---|
| Supplier | NFD |
| Generic | PA 46 |
| Material Status | Commercial: Active |
| Features | Heat Resistance, Good,Solvent resistance,Heat Stabilized |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | ASTM D792 |
| Water absorption rate | |||
| 24 hr | 1.2 | % | ASTM D570 |
| Shrinkage rate | |||
| MD：3.18 mm | 0.4 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 260 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.2 | % | ASTM D638 |
| Bending modulus | 15000 | MPa | ASTM D790 |
| bending strength | 340 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.18mm | 158 | J/m | ASTM D256 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.5 mm | HB | UL 94 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 8.00E+15 | Ohms∙cm | ASTM D257 |
| Dielectric strength | 22 | kV/mm | ASTM D149 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 288 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 3.40E-05 | cm/cm/℃ | ASTM D696 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| Melt Temperature | 246 to 316 | ℃ | |
| Mold temperature | 88 to 127 | ℃ | |
| drying temperature | 85 | ℃ | |
| Drying time | 4 to 8 | hr | |
| Temperature at the rear of the barrel | 282 to 316 | ℃ | |
| Temperature in the middle of the barrel | 282 to 316 | ℃ | |
| Front temperature of material barrel | 282 to 316 | ℃ | |
| Screw Speed | 40 to 80 | rpm | |
| Back pressure | 0.00 to 0.345 | MPa | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |