| About |
|---|
| TPC-ET Thermoplastic Elastomer. High Modulus, Nominal Shore D/15s 69. Natural colour&& |
| Product Description | |
|---|---|
| Supplier | Radici |
| Generic | TPC-ET |
| Material Status | Commercial: Active |
| Features | Good Rigidity |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 19 | g/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 10 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 115 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, unannealed | 60.0 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 210 | ℃ | ISO 306 |
| Melting temperature | 219 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | 249.0 | kN/m | DIN 53516 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore D, 3 seconds | 77 | ||
| Shore D, 15 seconds | 69 | ||
| Tensile modulus | 1350 | MPa | ISO 527-2/1A/1 |
| tensile strength | |||
| yield | 48.0 | MPa | |
| fracture | 29.0 | MPa | |
| 10% strain | 45.0 | MPa | |
| 100% strain | 32.0 | MPa | |
| Tensile strain | |||
| yield | 15 | % | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 350 | % | ISO 527-2/1A/50 |
| Bending modulus | 1260 | MPa | ISO 178 |
| bending strength | 50.0 | MPa | ISO 178 |
| abrasion resistance | 39.0 | mm³ | ASTM D1004 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature – hot air dryer | 110 | °C | |
| Drying time – hot air dryer | 2.0 to 4.0 | hr | |
| Dew Point – Hot Air Dryer | < -30 | °C | |
| Recommended maximum moisture content | 0.050 | % | |
| Processing (melt) temperature | 240 to 250 | °C | |
| Mold temperature | 30 to 50 | °C | |
| Injection speed | 中等 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.079 in/min |
| 3. 10°C/min |
| 4. 500V |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |