HFDB-4201 SC K

About
HFDB-4201 SC K is a long-life, cross linkable, low-density, polyethylene insulation compound of high cleanliness and purity developed especially for the insulation of High Voltage power cables. HFDB-4201 SC K is equipped with a non-migrating stabilizer providing high thermal stability, long term storage stability, and optimum cross-linking behavior. Applications: HFDB-4201 SC K is recommended especially for the insulation of High Voltage power transmission and distribution cables, <= 220kV. Specifications: Cables insulated with HFDB-4201 SC sb K would be expected to meet the requirements in the following standards when processed using state-of-the-art cable manufacturing practices: IEC: 62067, 60840 CENELEC: HD 632 S2 AEIC: CS9 ANSI/ICEA: 108-720-2004 GB/T 11017, GB/T 18890&&

About

HFDB-4201 SC K is a long-life, cross linkable, low-density, polyethylene insulation compound of high cleanliness and purity developed especially for the insulation of High Voltage power cables. HFDB-4201 SC K is equipped with a non-migrating stabilizer providing high thermal stability, long term storage stability, and optimum cross-linking behavior. Applications: HFDB-4201 SC K is recommended especially for the insulation of High Voltage power transmission and distribution cables, <= 220kV. Specifications: Cables insulated with HFDB-4201 SC sb K would be expected to meet the requirements in the following standards when processed using state-of-the-art cable manufacturing practices: IEC: 62067, 60840 CENELEC: HD 632 S2 AEIC: CS9 ANSI/ICEA: 108-720-2004 GB/T 11017, GB/T 18890&&

Product Description
Supplier	DOW
Generic	XLPE
Material Status	Commercial: Active
Availabilitys	North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.921	g/cm³	ISO 1183
Melt Flow Rate
130℃，2.16kg	0.30	g/10min	ISO 1133
humidity	< 200	ppm	Internal Method

MECHANICAL	Nominal value	Unit	Test method
tensile strength	20.0	MPa	IEC 60811-1-1
Tensile strain
fracture	500	%	IEC 60811-1-1

Aging performance	Nominal value	Unit	Test method
Change in Tensile Properties（10 days，150℃）	< 25	%	IEC 60811-1-1

THERMAL	Nominal value	Unit	Test method
thermosetting			IEC 811-2-1
Elongation under load: 200 ℃	< 100	%	IEC 60811-2-1
Permanent deformation: 200 ℃	< 5.0	%	IEC 60811-2-1

Electrical performance	Nominal value	Unit	Test method
Volume resistivity	> 1.0E+16	ohms·cm	IEC 60093
Dielectric strength	> 30	kV/mm	IEC 60243-1
Dielectric constant
1 MHz	< 2.30		IEC 60250
Dissipation factor
50 Hz	< 3.0E-4		IEC 60250

Supplementary information	Nominal value	Unit	Test method
Gottfert Elastograph（Torque）	0.60	N·m	ISO 6502
Reaction Speed – t90（180℃）	5.0	min	ISO 6502

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	115 to 140	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.