| HI-ZEX™ 640UF是一种高密度聚乙烯产品,。 它可以通过薄膜挤出进行加工,在北美洲、欧洲或亚太地区有供货。 典型应用领域为:电影。 特性包括: 高强度 快速成型周期&& |
| Product Description | |
|---|---|
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Quick molding cycle |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.947 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.21 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | < 1000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | 30 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 122 | ℃ | ISO 306 |
| Melting temperature | 131 | ℃ | ISO 11357-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D, molded | 64 | ISO 868 | |
| Tensile modulus | |||
| Compression Molding | 1000 | MPa | ISO 527-2 |
| tensile strength | |||
| Yield, molding | 23.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, molded | < 300 | % | ISO 527-2 |
| Bending modulus | |||
| Compression Molding | 1000 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |