| About |
|---|
| HIDEN® U050 is an Ultra High Molecular Weight Polyethylene material. It is available in Asia Pacific for compression molding or ram extrusion. Important attributes of HIDEN® U050 are: RoHS Compliant Good Processability High Molecular Weight Wear Resistant&& |
| Product Description | |
|---|---|
| Supplier | YUHWA |
| Generic | Ultra-high molecular weight polyethylene |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Ultra high molecular weight,Good wear resistance |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Apparent density | 0.45 | g/cm³ | ISO 60 |
| Average molecular weight | |||
| 10^6 g/mol | 5.00 | Internal Method | |
| Average particle size | 120 | µm | Internal Method |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 79.0 | ℃ | ASTM D648 |
| Melting peak temperature | 135 | ℃ | ASTM D3418 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 62 | ASTM D785 | |
| tensile strength | |||
| yield | > 16.7 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 300 | % | ASTM D638 |
| abrasion resistance | 100 | ISO 15527 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Shore D |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |