Hifax CA 1110 A3 LS1 BLACK

About
Hifax CA 1110 A3 LS1 BLACK medium high melt flow, 1,000 MPa flexural modulus, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a good combination of properties and processability. It is typically used for painted automotive bumper fascias.&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Good Rigidity,Excellent Processability,High impact resistance,High liquidity,Sprayable
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.970	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	14	g/10min	ASTM D1238

MECHANICAL	Nominal value	Unit	Test method
tensile strength
Yield, 23 ℃	17.0	MPa	ISO 527-2
Bending modulus
23℃	1000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	40	kJ/m²	ISO 180

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.