Hifax CA 1110 G4 LS/4

About
“Hifax” CA 1110 G4 LS/4 is a high melt flow, 10% mineral filled, UV stabilised high impact polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require high impact strength as well as good stiffness. This product has good UV resistance and very good aesthetics and is designed for outdoor application. It is not recommended for painted applications as surface defects could appear after painting. Shrinkage is lower (LS = low shrinkage) compared to Hifax CA 1110 G4. This grade is available in custom colour, pellet form.&&

About

“Hifax” CA 1110 G4 LS/4 is a high melt flow, 10% mineral filled, UV stabilised high impact polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require high impact strength as well as good stiffness. This product has good UV resistance and very good aesthetics and is designed for outdoor application. It is not recommended for painted applications as surface defects could appear after painting. Shrinkage is lower (LS = low shrinkage) compared to Hifax CA 1110 G4. This grade is available in custom colour, pellet form.&&

Product Description
Supplier	LyondellBasell
Generic	PP copolymer
Material Status	Commercial: Active
Features	Good Rigidity,Weather resistance is good,Good surface appearance,High impact resistance,High liquidity,Low contractility,Nontoxicity,Impact copolymer
Availabilitys	North America,Latin America,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.980	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	16	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	18.0	MPa	ISO 527-2
Bending modulus	1150	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180/1A
-30℃	4.7	kJ/m²	ISO 180-1A
-20℃	5.5	kJ/m²	ISO 180-1A
23℃	45	kJ/m²	ISO 180-1A

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	73.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	118	℃	ISO 306/A50

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.