Hifax CA 207 A

About
Hifax CA 207 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It is suitable for injection molding applications as well as for wire & cable extrusion process. As an impact modifier for compounding applications, it can be blended with other polyolefinic resins for a better shrinkage control and to improve the low temperature impact resistance. It does not contain any slip nor anti-blocking agents. The grade is available in natural pellet form.&&

About

Hifax CA 207 A is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell’s proprietary Catalloy process technology. It is suitable for injection molding applications as well as for wire & cable extrusion process. As an impact modifier for compounding applications, it can be blended with other polyolefinic resins for a better shrinkage control and to improve the low temperature impact resistance. It does not contain any slip nor anti-blocking agents. The grade is available in natural pellet form.&&

Product Description
Supplier	LyondellBasell
Generic	聚烯烃，共挤薄膜用聚烯烃
Material Status	Commercial: Active
Features	High impact resistance,Good Dimensional Stability,Good Electrical Properties,High Heat Resistance,Good wear resistance,low-temperature impact resistance
Availabilitys	Africa & Middle East ,North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.900	g/cm³	ISO 1183/A
Melt Flow Rate
230℃，2.16kg	7.5	g/10min	ISO 1133
Shrinkage rate
3.2 mm，48 hrs	0.60	%	ISO 294-4

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shore D, 15 seconds	50		ISO 868
tensile strength
fracture	22.0	MPa	ISO 527-2
yield	14.0	MPa	ISO 527-2
Tensile strain
fracture	> 800	%	ISO 527-2
yield	20	%	ISO 527-2
Bending modulus	500	MPa	ISO 178

elastic body	Nominal value	Unit	Test method
tear strength	122	kN/m	ASTM D624

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
-40℃	10	kJ/m²	ISO 180-1A
Dart impact equipped with measuring instruments			ASTM D3763
-40℃，Ductile Failure	23.0	J	ASTM D3763
23℃，Ductile Failure	16.0	J	ASTM D3763

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	60.0	℃	ISO 75-2/B
Vicat Softening Temp
A50	94.0	℃	ISO 306/A50
Melting temperature
DSC	162	℃	ISO 3146

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.