| About |
|---|
| Hifax CB 1183 A XHS BLACK is a 20% talc filled PP copolymer, with high impact resistance and very low UV resistance. Product is available in black color, pellet form. This grade is not intended for medical, pharmaceutical, food and drinking water applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | High impact resistance,Sprayable,Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 6.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 12.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 50 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1850 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 5.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 100 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 134 | ℃ | ISO 306/A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |