Hifax DX277 - SOLIAO

About
Hifax DX277 medium high melt flow, 1,000 MPa flexural modulus, thermoplastic elastomeric olefin (TEO) nanocomposite has an excellent balance of properties and processability. It is characterized by an exceptional impact/stiffness balance, which is attainable at very low density. As a result, parts molded from DX277 are light in weight and exhibit good toughness characteristics.&&

Product Description
Supplier	LyondellBasell
Generic	Polyolefin Elastomer
Material Status	Commercial: Active
Features	Good Rigidity,High impact resistance,Good Dimensional Stability,Sprayable,Low density
Availabilitys	North America
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.910	g/cm³	ISO 1183
Melt Flow Rate
230℃，2.16kg	13	g/10min	ASTM D1238
230℃，2.16kg	13	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
tensile strength
yield	18.0	MPa	ISO 527-2
Tensile strain
yield	12	%	ISO 527-2
Bending modulus	1000	MPa	ISO 178

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch			ISO 180
-40℃	4.7	kJ/m²	ISO 180
23℃	36	kJ/m²	ISO 180

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
1.8 MPa, unannealed	49.0	℃	ISO 75-2/A
0.45 MPa, unannealed	78.0	℃	ISO 75-2/B
Linear coefficient of thermal expansion
MD：-30~100℃	6.8E-5	1/℃	ISO 11359-2
MD：-30~100℃	6.8E-5	1/℃	ASTM E228

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.