| About |
|---|
| Hifax TKS 428P G22866 is an unfilled PP copolymer, with excellent impact/stiffness balance, good flowability, high UV resistance and very good surface appearance. Formula is improved to offer better aspect, especially on tiger stripes. Advanced technologies allowed for a significant reduction of mineral filler which contributed to the reduction of final part weight. The product is also available in other color matched, pellet form. This grade is delivered in G22866 color version.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP copolymer |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Good surface appearance,High impact resistance,Good liquidity,Low density,Copolymer |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 18.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1100 | MPa | ISO 178-A |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 6.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 无断裂 | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 131 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 73.0 | ℃ | ISO 306/A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 0.039 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |