| Hifax TRC 779X BLK high melt flow, 1,700 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It is typically used for multiple automotive exterior applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | Polyolefin Elastomer |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High liquidity |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 25 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 18.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 5.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1700 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -40℃ | 6.5 | kJ/m² | |
| 23℃ | 46 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| -40℃，3.20 mm | 23.0 | J | ASTM D3763 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.22 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |