| About |
|---|
| Hifax TYC 1168P GXH GLOB BLK very high melt flow for easy and fast molding and has low density, which reduces part weight. It has good stiffness and excellent cold temperature impact. It is typically used for mold-in color exterior trim and fascia applications.&& |
| Product Description | |
|---|---|
| Supplier | LyondellBasell |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Good Dimensional Stability,High liquidity,Good liquidity,Low contractility,Quick molding cycle,Low density,low-temperature impact resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.980 | g/cm³ | ISO 1183/A |
| Melt Flow Rate | |||
| 230℃，2.16kg | 35 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 23 ℃ | 18.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | > 500 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1600 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 5.1 | kJ/m² | |
| 23℃ | 54 | kJ/m² | |
| Dart impact equipped with measuring instruments | |||
| -30℃，3.20 mm | 22.0 | J | ASTM D3763 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 7.22 ft/sec |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |