| About |
|---|
| HiFill® ABS GF60 LE is an Acrylonitrile Butadiene Styrene (ABS) product filled with 60% glass fiber. It can be processed by injection molding and is available in North America. Typical application: Food Contact Applications. Primary characteristic: flame rated.&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Low extract,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.62 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.050 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.080 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 69 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 3.2 mm | 320 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 113 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 107 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 1.3E-5 | 1/℃ | ASTM D696 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 125 | ASTM D785 | |
| tensile strength | |||
| fracture | 117 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 2.0 | % | ASTM D638 |
| Bending modulus | 12800 | MPa | ASTM D790 |
| bending strength | 145 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 77 to 88 | °C | |
| Drying time | 2.0 to 16 | hr | |
| Barrel rear temperature | 216 to 232 | °C | |
| Barrel middle temperature | 221 to 238 | °C | |
| Barrel front temperature | 210 to 221 | °C | |
| Nozzle temperature | 199 to 221 | °C | |
| Processing (melt) temperature | 232 to 260 | °C | |
| Mold temperature | 71 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |