| About |
|---|
| HiFill® PA6/6 GF33 HS L is a Polyamide 66 (Nylon 66) product filled with 33% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Heat Stabilizer Lubricated&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Lubricating,Heat Stabilized,HB |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.37 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.40 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.55 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 120 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 254 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 260 | ℃ | ASTM D648 |
| Melting temperature | 262 | ℃ | |
| Linear coefficient of thermal expansion | |||
| MD | 3.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric strength | 18 | kV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | HB | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 172 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 4.0 | % | ASTM D638 |
| Bending modulus | 8960 | MPa | ASTM D790 |
| bending strength | 234 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 121 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.12 | % | |
| Barrel rear temperature | 282 to 293 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 277 to 288 | °C | |
| Nozzle temperature | 282 to 293 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 54 to 93 | °C | |
| Injection speed | Moderate-Fast | ||
| Back pressure | 0.345 to 0.689 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |