| About |
|---|
| Polycarbonate 10% Glass Fibers, Low Extractable&& |
| Product Description | |
|---|---|
| Generic | Polycarbonate |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good flexibility,Good Dimensional Stability,High Heat Resistance,Fatigue resistance |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.28 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.30 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.13 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，6.4mm | 96 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 149 | ℃ | |
| 1.8 MPa, unannealed | 141 | ℃ | |
| 1.5 mm | 75.0 | ℃ | |
| 3.0 mm | 75.0 | ℃ | |
| Relative temperature index | |||
| Electrical performance | |||
| Impact mechanical performance | |||
| 1.50 mm | 75.0 | ℃ | |
| 3.00 mm | 75.0 | ℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 75 | ASTM D785 | |
| Tensile modulus | |||
| 23℃ | 4480 | MPa | ASTM D638 |
| tensile strength | |||
| Fracture, 23 ℃ | 82.7 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 3.5 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 4140 | MPa | ASTM D790 |
| bending strength | |||
| Fracture, 23 ℃ | 124 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 121 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 299 to 316 | °C | |
| Barrel middle temperature | 310 to 343 | °C | |
| Barrel front temperature | 316 to 332 | °C | |
| Nozzle temperature | 310 to 332 | °C | |
| Processing (melt) temperature | 304 to 329 | °C | |
| Mold temperature | 71 to 88 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |