| About |
|---|
| HiFill® POM CO 0167 S2 LE is an Acetal (POM) Copolymer product filled with metal. It can be processed by injection molding and is available in North America. Typical application: Food Contact Applications. Primary characteristic: copolymer.&& |
| Product Description | |
|---|---|
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Low extract,Copolymer,Metal Detectable |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 9.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD：3.2 mm | 1.6 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.20 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 59 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 110 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.2E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 51.7 | MPa | ASTM D638 |
| Tensile strain | |||
| yield | 40 | % | ASTM D638 |
| Bending modulus | 3030 | MPa | ASTM D790 |
| bending strength | 82.7 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 100 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 71 | °C | |
| Drying time | 1.0 | hr | |
| Barrel rear temperature | 177 to 193 | °C | |
| Barrel middle temperature | 188 to 210 | °C | |
| Barrel front temperature | 182 to 199 | °C | |
| Nozzle temperature | 177 to 204 | °C | |
| Processing (melt) temperature | 193 to 216 | °C | |
| Mold temperature | 82 to 121 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |