| About |
|---|
| HiFill® PP GF15 CC is a Polypropylene product filled with 15% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: Flame Rated Chemically Coupled&& |
| Product Description | |
|---|---|
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good liquidity,Ultra high toughness |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.02 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD：3.2 mm | 0.55 | % | ASTM D995 |
| Water absorption rate | |||
| 23℃，24hr | 0.010 | % | ASTM D570 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Linear coefficient of thermal expansion | 4.5E-3 | cm/cm/℃ | ASTM D696 |
| melting point | 163 | ℃ | |
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ASTM D648 |
| 1.8 MPa, unannealed | 152 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 4.0E+16 | Ω.cm | ASTM D257 |
| Insulation strength | |||
| 20.9 | KV/mm | ASTM D149 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| – | HB | UL-94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | 112 | R 级 | ASTM D785 |
| bending strength | 97.2 | MPa | ASTM D790 |
| Tensile strain | |||
| tensile strength | 62.1 | MPa | ASTM D638 |
| Bending modulus | |||
| 23℃ | 2900 | MPa | ASTM D790 |
| yield | 4.7 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | 85.4 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | 587 | J/m | ASTM D256 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method A (Short-Time) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |