| HIPOL™ J940是一种聚丙烯扩冲击共聚物(PP Impact Copoly)材料,。 该产品在亚太地区有供货,加工方式为:注射成型。 HIPOL™ J940的主要特性有: 阻燃/额定火焰 共聚物 加工性能良好 耐冲击 HIPOL™ J940的典型应用领域为:工程/工业配件&& |
| Product Description | |
|---|---|
| Supplier | Mitsui |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Block Copolymer,HB |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 55 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 28.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 50 | % | ASTM D638 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 20 | J/m | |
| 0℃ | 39 | J/m | |
| 23℃ | 64 | J/m |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, unannealed | 115 | ℃ | |
| 1.8 MPa, unannealed | 55.0 | ℃ | |
| Vicat Softening Temp | 150 | ℃ | ASTM D1525 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.57 mm，ALL | HB | UL 94 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |