| HiPrene® HT42 is a medium melt flow, 20% mineral filled polypropylene compound. This material is high stiffness and it is primarly designed for Home Appliance Parts but is suitable for other parts in automotive industry.&& |
| Product Description | |
|---|---|
| Supplier | GS Caltex |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | processability,Good Rigidity,Mineral filler,High Heat Resistance,high-rigidity |
| Availabilitys | Europe,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| 1.04 | g/cm³ | ASTM D792 | |
| Melt Flow Rate | |||
| 2.16Kg，230℃ | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile strength | |||
| Yield yld | 36 | MPa | ASTM D638 |
| Tensile Elongation | 75 | % | ASTM D638 |
| Flexural Modulus | 2650 | MPa | ASTM D790 |
| Rockwell hardness | 102 | R Scale | ASTM D-785 |
| Flexural strength | 55 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 55 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 1.80 MPa | 141 | ℃ | ASTM D648 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Injection Molding | 40-80 | ℃ | |
| Back pressure | 10-20 | bar | |
| Holding pressure | 20-80 | bar | |
| Mold temperature | 25-50 | ℃ | |
| Screw speed | 低速to高速 | ||
| Injection speed | 低速to中速 | ||
| Rear Temperature | 190-210 | ℃ | |
| Middle Temperature | 190-220 | ℃ | |
| Front Temperature | 200-240 | ℃ | |
| Nozzle temperature | 210-250 | ℃ | |
| Melt Temperature | 200-250 | ℃ | |
| Injection pressure | 80-150 | bar | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |