| HiPrene® MR71E is a high melt flow, 15% mineral filled polypropylene compound. The grade has been specifically designed for moulding large complex parts that require high impact strength as well as good stiffness. This product is paintable.&& |
| Product Description | |
|---|---|
| Supplier | GS Caltex |
| Generic | PP not specified |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,High liquidity,Sprayable |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Flow Rate | 42 | g/10min | ISO 1133 |
| Ash Content | |||
| 600℃ | 13 to 17 | % | ISO 3451-1A |
| Volatiles | % | Internal Method | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 15.0 | MPa | ISO 527-2/1A/50 |
| Nominal tensile fracture strain | 25 | % | ISO 527-2/1A/50 |
| Bending modulus | 1300 | MPa | ISO 178/B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 35 | kJ/m² | ISO 180-A |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Procedure A |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |