| Hiprolon® 70 MNNHL G30 is a polyamide 6.10 produced from a renewable source and reinforced with 30% glass fiber. This natural grade is designed for injection molding.&& |
| Product Description | |
|---|---|
| Supplier | Arkema |
| Generic | PA610 |
| Material Status | Commercial: Active |
| Features | Renewable resources |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Shrinkage rate | ISO 294-4 , ISO 2577 | ||
| TD | 1.0 | % | ISO 294-4，ISO 2577 |
| MD | 0.50 | % | ISO 294-4，ISO 2577 |
| Water absorption rate | |||
| Equilibrium, 23 ℃, 50% RH | 0.80 | % | ISO 62 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8300 | MPa | ISO 527-2 |
| tensile strength | |||
| yield | 150 | MPa | ISO 527-2 |
| Tensile strain | |||
| fracture | 5.0 | % | ISO 527-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | ISO 179/1eA |
| 23℃ | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | ISO 179/1eU | ||
| -30℃ | 89 | kJ/m² | ISO 179/1eU |
| 23℃ | 90 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 221 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 210 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 217 | ℃ | ISO 306 |
| Melting temperature | 222 | ℃ | ISO 11357-3 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Compared to the leakage tracing index | > 600 | V | IEC 60112 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA 610, MHLR, 27-080, GF 30 | ISO 1874 | |
| Renewable Carbon Conent | > 60 | % | ASTM D6866 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 260 to 300 | °C | |
| Mold temperature | 60 to 110 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |