| About |
|---|
| HIVAL® HG6 Black is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in North America for injection molding. Important attributes of HIVAL® HG6 Black are: RoHS Compliant BPA Free Impact Resistant Rigid Typical applications include: Caps/Lids/Closures Consumer Goods Containers Household Applications Sporting Goods&& |
| Product Description | |
|---|---|
| Supplier | Nexeo |
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | High impact resistance,Good liquidity,High Heat Resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.04 | g/cm³ | ASTM D1505 |
| Melt Volume Rate | |||
| 230℃，3.8 kg | 4.80 | cm³/10min | ASTM D1238 |
| 220℃，10 kg | 19.0 | cm³/10min | ISO 1133 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 300 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 77.8 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 90.6 | ℃ | ASTM D648 |
| Vicat Softening Temp | 95.6 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 2300 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 45.0 | MPa | ASTM D638 |
| Bending modulus | 2300 | MPa | ASTM D790 |
| bending strength | 65.0 | MPa | ASTM D790 |
| Rockwell hardness | |||
| R-level | 103 | ASTM D785 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 77 to 79 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Barrel rear temperature | 199 to 232 | °C | |
| Barrel middle temperature | 204 to 232 | °C | |
| Barrel front temperature | 218 to 260 | °C | |
| Nozzle temperature | 218 to 260 | °C | |
| Processing (melt) temperature | 218 to 274 | °C | |
| Mold temperature | 27 to 49 | °C | |
| Injection pressure | 2.76 to 10.3 | MPa | |
| Back pressure | 1.03 to 3.45 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |