| Good Processability Good ESCR PE 100 (MRS 10)&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High ESCR |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.040 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 126 | ℃ | ASTM D1525 |
| Oxygen sensing time | |||
| 200℃ | > 30 | min | ISO 10837 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 57 | ASTM D785 | |
| tensile strength | |||
| yield | 21.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 700 | % | ASTM D638 |
| Bending modulus | 883 | MPa | ASTM D790 |
| Hydrostatic strength | ISO 1167 | ||
| 12.4 MPa：20℃ | > 200 | ISO 1167 | |
| 5.0 MPa：80℃ | > 5000 | ISO 1167 | |
| 5.5 MPa：80℃ | > 1000 | ISO 1167 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |