| About |
|---|
| FL7000 is manufactured to be processed in conventional blown film equipment by CSTR Slurry process technology. Thanks to Bi-modal design of molecular composition, 7000F offer both excellent processability and superior mechanical properties.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Inoxidizability,Bimodal molecular weight distribution |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.035 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F50 | > 1000 | hr | ASTM D1693 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| fracture | 31.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 981 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | No Break | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |