| HIVOREX M7100用于管材挤出成型，ISO PE100（MRS 10）级，具有良好的加工性，良好的机械性能。 |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.06/0.25 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | NB | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 125 | ℃ | ASTM D1525 |
| Oxygen induction time (200 ℃) | >30 | min | ISO/TR 10837 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 22.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | ≥700 | % | ASTM D638 |
| Bending modulus | 834 | MPa | ASTM D790 |
| R-level | 57 | ASTM D785 | |
| ESCR(Environmental Stress Cracking Resistance) | >1000 | F50 Hours | ASTM D1693 |
| Hydrostatic pressure test | ISO 1167 | ||
| 12.4MPa (20℃) | >100 | hr | ISO 1167（>100） |
| 5.4MPa (80℃) | >165 | hr | ISO 1167(>165) |
| 5.0MPa (80℃) | >1000 | hr | ISO 1167(>1000) |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |