| About |
|---|
| MF5000 is manufactured to be processed in flat yarn for tarpaulin by CSTR Slurry process technology. MF5000 is ideally suited for use in monofilament application. MF5000 offers good stretching, spinning, high strength property and melting stability.&& |
| Product Description | |
|---|---|
| Supplier | LOTTE |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Inoxidizability,Higher melt stability |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.954 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.95 | g/10min | ASTM D1238 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 200 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 74.0 | ℃ | ASTM D648 |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 50 | ASTM D785 | |
| tensile strength | |||
| fracture | 31.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 500 | % | ASTM D638 |
| Bending modulus | 981 | MPa | ASTM D790 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |