| About |
|---|
| High toughness&& |
| Product Description | |
|---|---|
| Supplier | Shunde Hones |
| Generic | PPS |
| Material Status | Commercial: Active |
| Features | Good flexibility,V-0 |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| MECHANICAL | Nominal value | Unit | Test method |
| tensile strength | 105 | MPa | Internal Method |
| Tensile strain | |||
| fracture | 1.5 | % | Internal Method |
| Bending modulus | 8000 | MPa | Internal Method |
| bending strength | 180 | MPa | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 235 | ℃ | Internal Method |
| Linear coefficient of thermal expansion | ISO 11359-2 | ||
| MD | 2.0E-5 | 1/℃ | ISO 11359-2 |
| TD | 4.0E-5 | 1/℃ | ISO 11359-2 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 2.0E+17 | ohms | IEC 60093 |
| Volume resistivity | 3.0E+16 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 3 mm | 16 | kV/mm | IEC 60243-1 |
| Compared to the leakage tracing index | 125 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| PHYSICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | Internal Method |
| Shrinkage rate | Internal Method | ||
| MD：2.0 mm | 0.30 | % | Internal Method |
| TD：2.0 mm | 0.60 | % | Internal Method |
| Water absorption rate | |||
| 23℃，24hr | 0.010 | % | ISO 62 |
| Apparent viscosity of melt | |||
| 310℃ | 350 | Pa·s | ISO 11443 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |